<p id="v7nnl"></p>
<p id="v7nnl"></p>

<p id="v7nnl"></p><pre id="v7nnl"><output id="v7nnl"></output></pre>

<p id="v7nnl"><delect id="v7nnl"><listing id="v7nnl"></listing></delect></p>
<pre id="v7nnl"><output id="v7nnl"><menuitem id="v7nnl"></menuitem></output></pre>

<p id="v7nnl"><delect id="v7nnl"><menuitem id="v7nnl"></menuitem></delect></p>

<pre id="v7nnl"></pre>
<pre id="v7nnl"><delect id="v7nnl"><menuitem id="v7nnl"></menuitem></delect></pre>

<p id="v7nnl"><output id="v7nnl"></output></p>
<pre id="v7nnl"></pre>

<p id="v7nnl"><output id="v7nnl"></output></p>
<p id="v7nnl"></p>
<p id="v7nnl"></p>

<p id="v7nnl"></p>
<p id="v7nnl"></p>
<p id="v7nnl"></p>
<p id="v7nnl"><delect id="v7nnl"><listing id="v7nnl"></listing></delect></p>

<p id="v7nnl"><output id="v7nnl"></output></p>
<output id="v7nnl"><output id="v7nnl"><menuitem id="v7nnl"></menuitem></output></output>
<pre id="v7nnl"><p id="v7nnl"></p></pre>
边亲边做边娇喘视频
大口径厚壁方管厂
您当前的位置:大口径厚壁方管厂 > 厚壁方管市场 > 正文碳化物形成元素强烈推迟珠光体转变
 
碳化物形成元素强烈推迟珠光体转变
来源:/ 浏览次数:

钢中合金元素使Ms点温度不断下降时,马氏体的形貌和微观结构将发生变化。低碳合金钢中马氏体的金相形貌呈片状,微观上是具有位错亚结构的板条马氏体。高碳高合金钢中马氏体的金相形貌是针状,微观上是具有孪晶亚结构的针状马氏体。

对过冷奥氏体恒温转变曲线的影响合金元素的影响综合表现在合金元素对过冷奥氏体恒温转变曲线上。碳化物形成元素(钒、钛、铌、钨、钼)强烈推迟珠光体转变,对贝氏体转变推迟较少,同时升高珠光体转变温度范围,降低贝氏体转变温度Bs点,使两个转变的C曲线分开,出现两个独立的C曲线。较弱的碳化物形成元素(铬、锰)都有强烈推迟珠光体和贝氏体转变,而推迟贝氏体转变作用更强烈,其过冷奥氏体恒温转变曲线也出现两个独立的C曲线。

非碳化物形成元素硅和铝都推迟两种转变,对贝氏体转变推迟作用更显著。非碳化物形成元素镍推迟珠光体转变作用大于推迟贝氏体转变。低镍含量钢与碳钢相似,只出现珠光体和贝氏体转变相重叠的一个C曲线,高镍含量钢中珠光体转变被抑制,仅在500℃以下出现贝氏体转变。晶界偏聚元素磷、硼和稀土也推迟珠光体转变,对过冷奥氏体恒温转变曲线的形状影响不大。

 